| 特性級別 | 增韌級|||耐低溫|||耐老化||| |
| 牌號 | 200-3 |
| 加工級別 | 注墮級||| |
| 品名 | |
| 廠家(產地) | LG-DOW |
| 用途級別 | 通用級|||食品級||| |
產品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動速率 | 230℃/3.8kg | ASTM D-1238 | 12 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 模具收縮率 | Flow,3.20mm | ASTM D-955 | 0.50-0.80 | % | |
| 機械性能 | 拉伸模量 | ASTM D-638 | 2480 | MPa | |
| 拉伸屈服強度 | ASTM D-638 | 46.9 | MPa | ||
| 拉伸斷裂強度 | ASTM D-638 | 35.9 | MPa | ||
| 拉伸屈服伸長率 | ASTM D-638 | 2.0 | % | ||
| 拉伸斷裂伸長率 | ASTM D-638 | 18 | % | ||
| 彎曲模量 | 50.0mm Span | ASTM D-790 | 2620 | MPa | |
| 彎曲屈服強度 | 50.0mm Span | ASTM D-790 | 79.3 | MPa | |
| IZOD缺口沖擊強度 | 23℃ | ASTM D-256 | 240 | J/m | |
| 熱性能 | 熱變形溫度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 95.6 | ℃ |
| 熱變形溫度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 82.2 | ℃ | |
| 維卡軟化溫度 | ASTM D-1525 | 98.9 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000088 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000085 | cm/cm/℃ | |
| 燃燒性 | 1.52mm | UL 94 | HB | ||